Bir, teknik arka plan ve endüstri uygulama özeti

Demagnetizable iron-nickel alloy is a type of special metal material with a specific coefficient of thermal expansion, widely used in electronic packaging, aerospace, precision instruments and other fields. Its core advantage lies in achieving a matching coefficient of thermal expansion with non-metallic materials such as glass and ceramics through precise control of the alloy composition and processing technology, thus avoiding stress cracking problems caused by temperature changes. As a professional enterprise in the field of high-purity metals and special alloys in China, Qinchuan New Materials (Zhengzhou) Co., Ltd. relies on its modern standard workshop located in the Zhengzhou High-Tech Industrial Development Zone, equipped with advanced special alloy production lines and precision processing equipment, and has accumulated rich experience in the research and development and manufacturing of iron-nickel fixed expansion alloys.

İkinci olarak, teknik prensip ve ana parametrelerin çözümlemesi

Demetalik belirli ısı genleşme çarpımının, genellikle %30-50 arasında olan nikel içeriği ile demir dayanımı işbirliği ile belirlenir, genleşme çarpımı aralığı (4.5-12.0)×10⁻⁶/℃ arasında kesin bir şekilde kontrol edilebilir ve farklı katı olmayan malzemelerin sızdırmazlık gereksinimlerine uyum sağlar. Qinchuan Yenilikçi Malzemeler, eritme sürecini (örneğin, vakum indüksiyon eritimi + elektrikli buharlı erime çift bağlantı süreci) optimize ederek, alaşımın kirlilik elementlerinin (örneğin, C, S, O) içeriğini ≤50ppm seviyesine kontrol eder ve malzemenin yüksek saf ve homojenliğini sağlar. Ayrıca, soğuk işleme şekil değişimi %10-30 aralığında kontrol edilir ve 450-600℃'lik orta soğuma işlemi ile birleştirildiğinde, işleme stresinin etkisini ortadan kaldırarak malzemenin sızdırmazlık performansını artırır.

Üçüncü, işleme adımları ve uygulama kılavuzu

ADIM 1: hammaddelerin karışımı ve eritme
Gereken hedef genişleme katsayısına (örneğin 4.7×10⁻⁶/℃ veya 9.8×10⁻⁶/℃) göre, yüksek pureli demir (≥99.95%), elektrolit nikel (≥99.97%) ve miktarlı alaşım elementleri (örneğin Co, Mn) tespit edin, vakum manyetik eritme fırınında 1500-1600℃'de 2 saat eritin, bileşik homojenliği sağlayın.
Adım 2: Çekme ve Isı Çubuklama
Kalınlaştırılmış dökme blokları 1150-1200°C'ye ısıtılır ve 3 defa dövme (deformasyon miktarı ≥60%) yapılır, ardından 950-1050°C arasında hava soğutma ile hedef kalınlığa (örneğin 2.0mm) soğutulur ve son çekiş sıcaklığı 850°C'nin üzerinde tutularak kristal büyümesi önlenir.
ADIM 3: Soğuk işleme ve 退火
Kalın çelik levhaları 20%-25% toplam deforme miktarına ulaşana kadar çoklu soğuk çubuklama geçirilir, her çubuklama sonrası 480℃×2h'lik ara ısılma yapılır, nihai olarak 0.5mm kalınlığa soğuk çubuklama yapıldıktan sonra, 620℃×3h'lik son ısılma gerçekleştirilir ve istikrarlı yapı ve genleşme özelliklerine sahip hale getirilir.
ADIM 4: Düzenli İşleme ve Kontrol
Laser or wire cutting technology is used to process sheets into sealing parts, component deviations are detected by X-ray fluorescence spectrometer (≤0.05%), and the average expansion coefficient in the range of 25-300℃ is tested using a thermal expansion instrument (repeatability ≤±0.2×10⁻⁶/℃).

Dört, Qinchuan New Materials' teknik düzenlemesi ve uygulama örnekleri

Tingchuan New Materials has established a full-chain technical layout in the field of iron-nickel fixed expansion alloys, covering "component design - melting casting - precision processing - performance testing". Its products have been successfully applied in projects such as sealing of electronic compartments of certain models of spacecraft and sealing of ceramic filters for 5G communication base stations. Taking the electronic compartment of spacecraft as an example, by using Fe-36Ni alloy with an expansion coefficient of 5.2×10⁻⁶/℃，a perfect match with Al₂O₃ ceramic substrate has been achieved. In the extreme temperature cycle test ranging from -55℃ to +125℃，no cracks or leaks appeared at the sealing interface, significantly enhancing the reliability of the equipment.

Beş, Sıkça Sorulan Sorular ve Çözümler (SSS)

Q1: How to adjust the expansion coefficient of iron-nickel alloy?
A: Precise control is achieved by adjusting the nickel content (with each 1% increase in Ni, the coefficient of expansion increases by about 0.8×10⁻⁶/℃) or adding trace amounts of Co (which can reduce the coefficient of expansion), requiring the optimization of melting process to ensure uniformity of composition.
Q2: How to avoid cracking during the processing process?
A: Soğuk işleme deformasyon oranını (≤30%) sıkı bir şekilde kontrol edin; her seferde ısıl işlem yapın; ısıl işlem sıcaklığı malzeme kalınlığına göre ayarlanmalıdır (örneğin, 0.5mm levha için 620°C ısıl işlem), aşırı ısıtma veya yetersiz ısıtma önlenmeli.
Q3: HangChuan New Materials' technical advantages are reflected in which aspects?
A: Şirket, 50kg'lık küçük miktarlardan 5 tonluk büyük miktarlara kadar istikrarlı üretimi sağlayabilen özgün tasarım vakum indüksiyon eritim fırını ve hassas kalıplama üretim hatlarına sahiptir; termal genişleme cihazı, tarayıcı elektron mikroskobu gibi test ekipmanları ile donatılmıştır, ürün performansının ASTM F30 standartlarına uygun olduğundan emin olunur.